材料成分

>99.99%，High Purity， Mono-crystalline Al2O3 (KY)

晶向類型C-M

C-axis (0001) off-cut 0.5°~10°  ± 0.1° toward M (1-100)

晶向類型C-A

C-axis (0001) off-cut 0.5°~8° ± 0.1° toward A (11-20)

晶向類型A-M

A-axis (11-20) off-cut 0.5°~6° ± 0.1° toward M (1-100)

晶向類型A-C

A-axis (11-20) off-cut 0.5°~6° ± 0.1° toward C (0001)

晶向類型R-M

R-axis (1-102) off-cut 0.5°~6° ± 0.1° toward M (1-100)

晶向類型R-C

R-axis (1-102) off-cut 0.5°~6° ± 0.1° toward C (0001)

晶向類型M-C

M-axis (1-100) off-cut 0.5°~6° ± 0.1° toward C (0001)

直徑

50.8mm

100mm

150mm

厚度

430um

650um

1000um

定位邊晶向

A-plane ± 0.3°

定位邊長度

16mm

30mm

47.5mm

正面狀態(tài)

Epi-polished,Ra<0.3nm

反面狀態(tài)

SSP:Fine-ground,Ra=0.8-1.2um; DSP:Epi-polished,Ra<0.3nm

總厚度偏差TTV

<10 um

<20 um

<25 um

彎曲度BOW

-15～0 um

-25～0 um

-35～0 um

翹曲度WARP

<15 um

<30 um

<40 um

邊緣去除

≤2 mm

晶體結(jié)構(gòu)

六方晶體

禁帶寬度(eV)

/

熔點（℃）

2040℃

莫氏硬度(mohs)

9

熱導率(W·cm^-1·℃^-1)

0.46W·cm^-1·℃^-1

熱膨脹系數(shù)(℃^-1)

6.7*10-6 // C-axis
5.0*10-6 ⊥C-axis

晶格常數(shù)(nm)

a=4.76? c=12.99?

折射率

1.762~1.777

透過率

測試樣品：藍寶石：直徑76.2毫米×厚度4毫米
紫外線：波長200至380納米，透過率74%至84%
可見光：波長380至760納米，透過率85%
紅外線：波長760至1000納米，透過率85%
遠紅外線：波長大于1000納米，透過率80%至100%